Red iron oxide alkyd primer
Color: Red
Finish: Flat, matt
Product description:: It is used as an antioxidant with hardness and excellent adhesion for metal structures that they put in mild atmospheric conditions
Finish: Flat, matt
Product description:: It is used as an antioxidant with hardness and excellent adhesion for metal structures that they put in mild atmospheric conditions
Technical data:
| Description: | Alkyd based, rust preventing, corrosion resistant general purpose protective primer It has excellent adhesion flexibility and exceptional durability |
| Area of application: | On ferrous surface like steel structures, metal works etc. |
| Physical constants: | |
| Color: | red |
| Gloss: | matt, Flat |
| Viscosity: | 50-70 cup 6 |
| Specific gravity: | Max 1.6 gr/100cc |
| Solid: | 70-78 |
| Covering capacity: | 12-15 M2/lit |
| Drying time: | Touch dry: 1-2 Minutes/ Max: 45 Minutes Hard dry: 4-6hours/ Max 3 hours Dry to recoat: 24 hours |
| Application details: | |
| Method of application: | Brush, roller or spray |
| Thinning: | Thinner TC-9920 |
| Air Spray: | Nozzle orifice:0.38-0.53mm Nozzle pressure:120-150 bar |
| Film thickness: | Dry 40-50 microns Wet 75-90 microns |
| Surface Preparation: | Remove all corrosion, mill scale, dirt, grease etc. by blast cleaning, flame cleaning, scraping wire brushing or any other suitable technique. Ensure surface is absolutely dry at the time of painting or else rust will form underneath the paint film |
Red Lead alkyd primer
Color: orange
Finish: matt
Product description: This orange primer is used in metal structures. It has stability in environment corrosion and describable coverage in surface
Finish: matt
Product description: This orange primer is used in metal structures. It has stability in environment corrosion and describable coverage in surface
Technical data:
| Description: | Alkyd based primer containing red lead which is rust preventing for steel surface, It has excellent resistance against mild to moderate corrosive atmosphere |
| Area of application: | On ferrous surface like steel structures etc. |
| Physical constants: | |
| Color: | Orange |
| Gloss: | matt |
| Viscosity: | 50-70 sec cup 6 |
| Specific gravity: | 1.7-2.1 gr/100cc |
| Solid: | 70-78 |
| Covering capacity: | 12-15 M2/lit |
| Drying time: | Touch dry: 45 min Hard dry: 3 hours Dry to recoat: 24 hours |
| Application details: | |
| Method of application: | Brush, roller or spray |
| Thinning: | Thinner TC-9920 |
| Air Spray: | Nozzle orifice 1.2-2 mm Nozzle pressure 3-4 Bar |
| Airless Spray: | Nozzle orifice 0.38-0.53mm Nozzle pressure 120-150 bar |
| Film thickness: | Dry 40-50 microns Wet 75-90 microns |
| Surface Preparation: | Remove all corrosion, mill scale, dirt, grease etc. by blast cleaning, flame cleaning, scraping wire brushing or any other suitable technique. Ensure surface is absolutely dry at the time of painting or else rust will form underneath the paint film |
Zinc phosphate alkyd primer
Product description: It is used as the first layer into the multilayer systems of alkyd coating layer in environment of corrosive and industrial installation that exposed for the maximum temperature at 80 degrees Celsius
Technical data:
| Description: | Alkyd based zinc phosphate primer having good corrosion resistance. It has excellent adhesion and flexibility |
| Area of application: | On ferrous surface like steel structures etc. |
| Physical constants: | |
| Color: | Gray, other color on request |
| Gloss: | matt |
| Viscosity: | 50-70 cup 6 |
| Specific gravity: | 1.3 -1.6 gr/100cc |
| Solid: | 72-77 |
| Covering capacity: | 14-20 M2/lit |
| Drying time: | Touch dry:1-2 minutes Hard dry: 5-6hours Dry to recoat: 12 hours |
| Application details: | |
| Method of application: | Brush, roller or spray |
| Thinning: | Thinner TC-9920 |
| Air Spray: | nozzle orifice: 0.38-0.53m Nozzle pressure: 120-150 bar |
| Film thickness: | Dry 40-50 microns Wet 75-90 microns |
| Surface Preparation: | Remove all corrosion, mill scale, dirt, grease etc. by blast cleaning, flame cleaning, scraping wire brushing or any other suitable technique. Ensure surface is absolutely dry at the time of painting or else rust will form underneath the paint film |
Zinc chromate alkyd primer
Product description: It is used for anticorrosion primer for metal structures
Technical data:
| Description: | Alkyd based zinc chromate primer having good corrosion resistance. It has excellent adhesion and flexibility |
| Area of application: | On ferrous surface like steel structures etc. |
| Physical constants: | |
| Gloss: | matt |
| Viscosity: | 50-70 cup 6 |
| Specific gravity: | 1.3 -1.6 gr/100cc |
| Solid: | 72-77 |
| Drying time: | Touch dry: 1-2 minutes Hard dry: 5-6 hours Dry to recoat: 12 hours |
| Application details: | |
| Method of application: | Brush, roller or spray |
| Thinning: | Thinner TC-9920 |
| Air Spray: | Nozzle orifice 0.38-0.53 Nozzle pressure 120-150 Bar |
| Film thickness: | Dry 40-50 microns Wet 75-90 microns |
| Surface Preparation: | Remove all corrosion, mill scale, dirt, grease etc. by blast cleaning, flame cleaning, scraping wire brushing or any other suitable technique. Ensure surface is absolutely dry at the time of painting or else rust will form underneath the paint film |
Factory
Address: No21 - North Talash St - Industrial Estate of Mashhad - Mashhad - Iran
Tel: (+98511) 2453358 – 2453143
Fax: (+98511) 2453361
Center office
Address: No.269 - Mosala 13 St - Mosla Blv - Mashhad - Iran
Postal code: 9167685787
Tel: (+98511) 3642065 - 3648351
Fax: (+98511) 3647629